Study the Properties of Solution Processable CZTS Thin Films Induced by Annealing Treatment: Study of Annealing Time
Полная версия: 10.1134/S1063782620090110
Gani Shaikh R.A.1, More S.A.1, Bisen G.G.1, Ghosh S.S.1
1Optoelectronics Laboratory, Department of Physics, Kavayitri Bahinabai Chaudhari North Maharashtra University, Jalgao, Maharashtra, India
Email: ssghosh@nmu.ac.in
Поступила в редакцию: 13 мая 2020 г.
Выставление онлайн: 11 июня 2020 г.

Cu2ZnSnS4 is suitable for high-performance thin-film solar cell because of its high absorbance coefficient, presence of non-toxic elements, excellent optoelectronic properties, and a near-perfect direct band gap. The effect of thermal annealing time (1-4 hour) on the optical, morphological, and structural properties of Cu2ZnSnS4 coated through a simple solution processable method has been studied in the present work. All the CZTS films are crystalline in nature with kesterite structure as shown by X-ray diffraction studies. Crystallite size, strain, and dislocation density were calculated. However, no notable changes in these parameters were obtained by varying the annealing time in the above range. Field emission scanning electron microscopy images show good quality compact films with particle size in the order of 10-5 nm. Absorption spectroscopy results show an optical band gap of 1.46 eV. Raman spectroscopy was used to check binary or ternary phases present. It shows that the impurity phase decreases and the pure Cu2ZnSnS4 phase was obtained by increasing the annealing time to 3 and 4 hours. Keywords: Cu2ZnSnS4, thermal annealing, optical, characterization, Raman spectroscopy.

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.