Физика твердого тела

Авторам

Правила оформления публикаций

Вышедшие номера

2024
- 1 2 3 4 5 6 7 8 9 10
2023
- 1 2 3 4 5 6 7 8 9 10 11 12
2022
- 1 2 3 4 5 6 7 8 9 10 11 12
2021
- 1 2 3 4 5 6 7 8 9 10 11 12
2020
- 1 2 3 4 5 6 7 8 9 10 11 12
2019
- 1 2 3 4 5 6 7 8 9 10 11 12
2018
- 1 2 3 4 5 6 7 8 9 10 11 12
2017
- 1 2 3 4 5 6 7 8 9 10 11 12
2016
- 1 2 3 4 5 6 7 8 9 10 11 12
2015
- 1 2 3 4 5 6 7 8 9 10 11 12
2014
- 1 2 3 4 5 6 7 8 9 10 11 12
2013
- 1 2 3 4 5 6 7 8 9 10 11 12
2012
- 1 2 3 4 5 6 7 8 9 10 11 12
2011
- 1 2 3 4 5 6 7 8 9 10 11 12
2010
- 1 2 3 4 5 6 7 8 9 10 11 12
2009
- 1 2 3 4 5 6 7 8 9 10 11 12
2008
- 1 2 3 4 5 6 7 8 9 10 11 12
2007
- 1 2 3 4 5 6 7 8 9 10 11 12
2006
- 1 2 3 4 5 6 7 8 9 10 11 12
2005
- 1 2 3 4 5 6 7 8 9 10 11 12
2004
- 1 2 3 4 5 6 7 8 9 10 11 12
2003
- 1 2 3 4 5 6 7 8 9 10 11 12
2002
- 1 2 3 4 5 6 7 8 9 10 11 12
2001
- 1 2 3 4 5 6 7 8 9 10 11 12
2000
- 1 2 3 4 5 6 7 8 9 10 11 12
1999
- 1 2 3 4 5 6 7 8 9 10 11 12
1998
- 1 2 3 4 5 6 7 8 9 10 11 12
1997
- 1 2 3 4 5 6 7 8 9 10 11 12
1996
- 1 2 3 4 5 6 7 8 9 10 11 12
1995
- 1 2 3 4 5 6 7 8 9 10 11 12
1994
- 1 2 3 4 5 6 7 8 9 10 11 12
1993
- 1 2 3 4 5 6 7 8 9 10 11 12
1992
- 1 2 3 4 5 6 7 8 9 10 11 12
1991
- 1 2 3 4 5 6 7 8 9 10 11 12
1990
- 1 2 3 4 5 6 7 8 9 10 11 12
1989
- 1 2 3 4 5 6 7 8 9 10 11 12
1988
- 1 2 3 4 5 6 7 8 9 10 11 12

Сегнетоэлектрические релаксорные свойства образцов системы (1-2x)BiScO₃· xPbTiO₃· xPbMg_1/3Nb_2/3O₃ (0.30≤ x≤0.46)

DOI: 10.21883/FTT.2017.01.43947.431

Буш А.А.¹, Каменцев К.Е.¹, Бехтин М.А.¹, Сегалла А.Г.²

¹Московский государственный университет информационных технологий, радиотехники и электроники, Москва, Россия
²НИИ Элпа", Москва, Зеленоград, Россия

Email: aabush@yandex.ru

Поступила в редакцию: 6 ноября 2015 г.

Выставление онлайн: 20 декабря 2016 г.

PDF версия

Абстракт
Литература
Статистика просмотров

На керамических образцах системы твердых растворов (1-2x)BiScO₃· xPbTiO₃· xPbMg_1/3Nb_2/3O₃ (0.30≤ x≤0.46) со структурой перовскита выполнены рентгенографические, диэлектрические, пьезоэлектрические и пироэлектрические исследования. Найдено, что симметрия твердых растворов изменяется с ростом x от ромбоэдрической (x≤0.38) до тетрагональной (x≥0.42). Образцы с 0.30<x≤0.42 имеют характерные для сегнетоэлектриков-релаксоров свойства, проявляющиеся в наличии широкого пика на температурной зависимости диэлектрической проницаемости при T_mvarepsilon=390-440 K, положение которого смещается с частотой в сторону высоких температур, узких ненасыщенных петель диэлектрического гистерезиса, индуцированного электрическим полем перехода в сегнетоэлектрическое состояние при 318 K. Обнаруженные особенности диэлектрических, пьезо- и пироэлектрических свойств изученных твердых растворов объясняются принадлежностью их к сегнетоэлектрикам-релаксорам. Работа выполнена при поддержке Министерства образования и науки РФ (проект N 3.734.2014/К проектной части госзадания) и РФФИ (грант N 15-02-04647). DOI: 10.21883/FTT.2017.01.43947.431

R.E. Eitel, C.A. Randall, T.R. Shrout, P.W. Rehrig, W. Hackenberger, S.-E. Park. Jpn. J. Appl. Phys. 40, 5999 (2001)
R.E. Eitel, C.A. Randall, T.R. Shrout, S.-E. Park. Jpn. J. Appl. Phys. 41, (Pt 1), 2099 (2002)
Y. Shimojo, R. Wang, T. Sekiya, T. Nakamura, L.E. Cross. Ferroelectrics. 284, 121 (2003)
R.E. Eitel, Th.R. Shrout, C.A. Randall. Jpn. J. Appl. Phys. 43, 8146 (2004)
Y. Inaguma, A. Miyaguchi, M. Yoshida, T. Katsumata, Y. Shimojo, R. Wang, T. Sekiya. J. Appl. Phys. 95, 231 (2004)
R.E. Eitel, S.J. Zhang, T.R. Shrout, C.A. Randall, I. Levin. J. Appl. Phys. 96, 2828 (2004)
S. Zhang, C.A. Randall, T.R. Shrout. Jpn. J. Appl. Phys. 43, 6199 (2004)
S.J. Zhang, R.E. Eitel, C.A. Randall, T.R. Shrout, E.F. Alberta. Appl. Phys. Lett. 86, 262904 (2005)
S. Chen, X. Dong, C. Mao, F. Cao. J. Amer. Ceram. Soc. 89, 3270 (2006)
J. Chaigneau, J.M. Kiat, C. Malibert, C. Bogicevic. Phys. Rev. B 76, 094111 (2007)
C.J. Stringer, N.J. Donnelly, T.R. Shrout, C.A. Randall, E.F. Alberta, W.S. Hackenberger. J. Am. Ceram. Soc. 91, 1781 (2008)
T. Zou, X. Wang, W. Zhao, L. Li. J. Am. Ceram. Soc. 91, 121 (2008)
A. Sehirlioglu, A. Sayir, F. Dynys. J. Appl. Phys. 106, 014102 (2009)
А.А. Буш, К.Е. Каменцев, А.М. Лаврентьев, А.Г. Сегалла, Ю.К. Фетисов. Неорган. материалы 47, 865 (2011)
J. Chen, H. Shi, G. Liu, J. Cheng, S. Dong. J. Alloys Compd. 537, 280 (2012)
J. Chen, J. Cheng, S. Dong. J. Adv. Dielectrics 4, 1430002 (2014)
Б. Яффе, У. Кук, Г. Яффе. Пьезоэлектрическая керамика. Пер. с англ. Мир, M. (1974). 288 с
ОСТ 11 0444-87. Материалы пьезокерамические. Технические условия. Введены 01.01.88. Группа Э-10. 41 с
А.Я. Данцигер, О.Н. Разумовская, Л.А. Резниченко, В.П. Сахненко, А.Н. Клевцов, С.И. Дудкина, Л.А. Шилкина, Н.В. Дергунова, А.Н. Рыбянец. Многокомпонентные системы сегнетоэлектрических сложных оксидов: физика, кристаллохимия, технология. Аспекты дизайна пьезоэлектрических материалов. Изд-во Ростов. ун-та, Ростов н/Д (2001--2002). Т. 1. 408 с. Т. 2. 365 с
B.S. Kang, S.K. Choi, C.H. Park. J. Appl. Phys. 94, 1904 (2003)
Г.А. Смоленский, В.А. Боков, В.А. Исупов, Н.Н. Крайник, Р.Е. Пасынков, М.С. Шур. Сегнетоэлектрики и антисегнетоэлектрики. Наука, Л. (1971). 476 с
A.A. Bokov, Z.-G. Ye. J. Mater. Sci. 41, 31 (2006)
R. Skulski, P. Warwrzala, K. Cwikiel, D. Bochenek. J. Intell. Mater. Syst. Struct. 18, 1049 (2007)
R. Sommer, N.K. Yushin, J. J. van der Klink. Phys. Rev. B 48, 13230 (1993)
В.В. Гладкий, В.А. Кириков, Е.В. Пронина. ФТТ 45, 1238 (2003).

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.

Учредители

Издатель