Anomalous hysteresis loops of ferrimagnetic Gd-Co films of different thickness near the magnetic compensation temperature
Rusalina A. S.1, Lepalovskij V. N.1, Stepanova E. A. 1, Vas’kovskiy V. O. 1,2, Kurlyandskaya G. V. 1, Svalov A. V. 1
1Institute of Natural Sciences and Mathematics, Ural Federal University named after the First President of Russia B. N. Yeltsin, Yekaterinburg, Russia
2M.N. Mikheev Institute of Metal Physics, Ural Branch, Russian Academy of Sciences, Yekaterinburg, Russia
Email: Anastasia.Rusalina@urfu.ru, vladimir.lepalovsky@urfu.ru, elena.stepanova@urfu.ru, andrey.svalov@urfu.ru

PDF
Triple hysteresis loops were observed for amorphous ferrimagnetic Gd-Co films near the magnetic compensation temperature, which can be a consequence of both the spin-flop transition and the chemical composition gradient. In the work, an assessment of the possible chemical inhomogeneity of the films based on magnetic measurements was carried out and its relationship with the thickness of the samples was observed. Keywords: amorphous magnetic films, perpendicular magnetic anisotropy, ferrimagnetism, magnetic domain structure, magnetic hysteresis.
  1. A.E. Clark, E. Callen. J. Appl. Phys. 39, 5972 (1968)
  2. M.B. Jungfleisch, W. Zhang, A. Hoffmann. Phys. Lett. A 382, 865 (2018)
  3. Yu. Skourski, M.D. Kuz'min, K.P. Skokov, M. Richter, D. Eckert, I.S. Tereshina, K.-H. Muller. J. Magn. Magn. Mater. 290-291, 435 (2005)
  4. Becker, A. Tsukamoto, A. Kirilyuk, J.C. Maan, Th. Rasing, P.C.M. Christianen, A.V. Kimel. Phys. Rev. Lett. 118, 117203 (2017)
  5. M.D. Davydova, K.A. Zvezdin, J. Becker, A.V. Kimel, A.K. Zvezdin. Phys. Rev. B 100, 064409 (2019)
  6. T. Fu, S. Li, X. Feng, Y. Cui, J. Yao, B. Wang, J. Cao, Z. Shi, D. Xue, X. Fan. Phys. Rev. B 103, 064432 (2021)
  7. D. Chen, Y. Xu, S. Tong, W. Zheng, Y. Sun, J. Lu, N. Lei, D. Wei, J. Zhao. Phys. Rev. Mater. 6, 014402 (2022)
  8. M. Amatsu, S. Honda, T. Kusuda. IEEE Trans. Magn. 13, 1612 (1977)
  9. R.I. Tagirov, A.A. Glaser. FMM 46, 1, 75 (1978). (in Russian)
  10. T. Kobayashi, H. Tsuji, S. Tsunashima, S. Uchiyama. Jpn. J. Appl. Phys. 20, 11, 2089 (1981)
  11. V.O. Vaskovsky, V.V. Lesnykh, G.S. Kandaurova, T.H. Agamalian. FMM 59, 3, 470 (1985). (in Russian)
  12. A.V. Svalov, V.O. Vas'kovskiy, G.V. Kurlyandskaya. Phys. Met. Metallogr. 118, 13, 1263 (2017)
  13. A.V. Svalov, O.A. Adanakova, V.O. Vas'kovskiy, K.G. Balymov, A. Larranaga, G.V. Kurlyandskaya, R. Domingues Della Pace, C.C. Pla Cid. J. Magn. Magn. Mater. 459, 57 (2018)
  14. A.N. Sorokin, A.V. Svalov. Vacuum 46, 2, 1131995 (1995)
  15. K. Chen, D. Lott, F. Radu, F. Choueikani, E. Otero, Ph. Ohresser. Sci. Rep. 5, 18377 (2016)
  16. J.-L. Bello, D. Lacour, S. Migot, J. Ghanbaja, S. Mangin, M. Hehn. Appl. Phys. Lett. 121, 212402 (2022)

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.

Publisher:

Ioffe Institute

Institute Officers:

Director: Sergei V. Ivanov

Contact us:

26 Polytekhnicheskaya, Saint Petersburg 194021, Russian Federation
Fax: +7 (812) 297 1017
Phone: +7 (812) 297 2245
E-mail: post@mail.ioffe.ru