Effect of oxygen content "stabilization" in La0.8Sr0.2MnO3-delta films at post annealing in air
Nikolaenko Yu.M.1, Efros N.B.1, Fedyuk D.O.1, Reshidova I.Yu.1
1Donetsk Institute for Physics and Engineering, Donetsk, Ukraine
Email: nik@donfti.ru, bashacat1@gmail.com, fediukoleg@yandex.ru, reshidova@donfti.ru

PDF
The variation of oxygen content in the epitaxial La0.8Sr0.2MnO3-delta films of 12-75 nm thick onto NdGaO3 substrates was quantitatively investigated by indirect method during heat treatment procedure in air at temperature range 873-1073 K. The experimental time dependences of oxygen content variation were investigated theoretically with taking into account the effect of inhomogeneous diffusion of oxygen over the films thickness to provide optimal choice of temperature and duration of the heat treatment procedure. In films 25-75 nm thick, the effect of "stabilization" of the oxygen content (OC = 3) is revealed, which indicates the presence of an energy barrier that prevents the incorporation of an excess oxygen atom into the near-surface layer of the film at optimal conditions of heat treatment. Keywords: epitaxial films, strain, oxygen index, non-uniform oxygen diffusion.
  1. A. Abrutis, V. Plausinaitiene, V. Kubilius, A. Teiserskis, Z. Saltyte, R. Butkute, J.P. Senateur. Thin Solid Films 413, 1--2, 32 (2002)
  2. P.M. Leufke, A.K. Mishra, A. Beck, D. Wang, C. Kubel, H. Hahn, R. Kruk. Thin Solid Films 520, 5521 (2012)
  3. V.N. Varyukhin, Y.V. Medvedev, Y.M. Nikolaenko, A.B. Mukhin, B.V. Belyaev, V.A. Gritskikh, I.V. Zhikharev, S. V. Kara-Murza, N.V. Korchikova, A.A. Tikhii. PZhTF 35, 20, 19 (2009) (in Russian)
  4. S.I. Khartsev, P. Johnsson, A.M. Grishin. J. Appl. Phys. 87, 5, 2394 (2000)
  5. J.H. Kuo, H.U. Anderson, D.M. Sparlin. J. Solid State Chem. 83, 1, 52 (1989)
  6. Yu.M. Baykov, E.I. Nikulin, B.T. Melekh, V.M. Egorov. FTT 46, 11, 2018 (2004) (in Russian)
  7. A. Urushibara, Y. Moritomo, T. Arima, A. Asamitsu, G. Kido, Y. Tokura. Phys. Rev. B 51, 20, 14103 (1995)
  8. L. Malavasi, M.C. Mozzati, C.B. Azzoni, G. Chiodelli, G. Flor. Solid State Commun. 123, 321 (2002)
  9. Yu.M. Nikolaenko, A.N. Artemov, Yu.V. Medvedev, N.B. Efros, I.V. Zhikharev, I.Yu. Reshidova, A.A. Tikhii, S.V. Kara-Murza. J. Phys. D 49, 37, 375302 (2016)
  10. K. Nakamura, M. Xu, M. Klaser, G. Linker. J. Solid State Chem. 156, 1, 143 (2001)
  11. G.A. Ovsyannikov, A.M. Petrzhik, I.V. Borisenko, A.A. Klimov, V.V. Demidov, S.A. Nikitov. ZhETF 135, 1, 56 (2009) (in Russian)
  12. F. Tsui, M.C. Smoak, T.K. Nath, C.B. Eom. Appl. Phys. Lett. 76, 17, 2421 (2000)
  13. Yu.M. Nikolaenko, N.B. Efros, A.N. Artemov. ZhTF, 91, 12, 1957 (2021) (in Russian)
  14. L. Yin, C. Wang, Q. Shen, L. Zhang. RSC Advances 6, 96093 (2016)
  15. Yu.M. Nikolaenko, A.B. Mukhin, V.A. Chaika, V.V. Burkhovetsky. ZhTF, 80, 8, 115 (2010) (in Russian)
  16. Yu.M. Nikolaenko, A.S. Korneevets, N.B. Efros, V.V. Burkhovetsky, I.Yu. Reshidova. Pis'ma v ZhTF, 45, 13, 44 (2019) (in Russian)
  17. Y. Feng, K. Jin, L. Gu, X. He, C. Ge, Q. Zhang, M. He, Q. Guo, Q. Wan, M. He, H. Lu, G. Yang. Sci. Rep. 6, 22382 (2016)
  18. J.Z. Sun, D.W. Abraham, R.A. Rao, C.B. Eom. Appl. Phys. Lett. 74, 20, 3017 (1999)
  19. S. Koohfar, Y. Ozbek, H. Bland, Z. Zhang, D.P. Kumah. J. Appl. Phys. 129, 055301 (2021)

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.

Publisher:

Ioffe Institute

Institute Officers:

Director: Sergei V. Ivanov

Contact us:

26 Polytekhnicheskaya, Saint Petersburg 194021, Russian Federation
Fax: +7 (812) 297 1017
Phone: +7 (812) 297 2245
E-mail: post@mail.ioffe.ru