Relationship of Mg2Si Phase-Content and Thermal Expansion Properties of Mg-Si and Mg-Si-Ca Alloys
Полная версия: 10.1134/S1063783419120588
Wu S.1, Guo T.1, An P.1, Zhou X.1, Lu S.1
1State Key Lab of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, China
Email: ssw636@hust.edu.cn
Поступила в редакцию: 16 июля 2019 г.
Выставление онлайн: 19 ноября 2019 г.

The thermal expansion properties of Mg-xSi (x=1 wt.%, 1.38 wt.%, 2 wt.%, 3 wt.%, and 4 wt.%) binary alloys and Mg-4Si-yCa (y=0.2 wt.%, 0.4 wt.%, 0.6 wt.%, 0.8 wt.%, and 1.0 wt.%) alloys over a temperature range of 25-300oC were systematically studied. The results show that the Mg-Si binary alloys consist of alpha-Mg and Mg2Si phases. The volume fraction of Mg2Si phase increases with the increase of Si content in Mg-Si alloys, from 30.72% to 46.50% when Si content increases from 1 wt.% Si to 4 wt.% Si. The coefficient of thermal expansion (CTE) of Mg-xSi binary alloys decreases with the increase of Mg2Si volume fraction. The addition of Ca element to Mg-4Si alloys has an obvious modification effect on the Mg2Si phase. When the Ca content increases constantly, the CTE of the Mg-4Si-Ca alloys increases at first, then it continues to decline. The mechanism is mainly related14ks to the formation of the CaMgSi phase. Keywords: Mg-Si alloy, Mg2Si phase, modification, thermal expansion.

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.